Paper: Refined cyclic R-curve determination through residual crack tip stress reduction by annealing

Today, the propagation behavior of small fatigue cracks in high-strength materials such as high speed steels used to make metalworking tools is not understood sufficiently to boost their fatigue properties by knowledge-based design. That’s why Lukas Walch, Thomas Klünsner, Gerald Ressel, and Stefan Marsoner at Materials Center Leoben, as well as other researchers at Erich Schmid Institute and voestalpine Böhler Edelstahl developed a technique that enables a far more accurate determination of the resistance to fatigue crack propagation. This property would otherwise remain inaccessible for the future design of the new, more damage-resistant high speed steel grades we need for the resource-efficient manufacture of our everyday goods.

For further information, please visit the following website: https://authors.elsevier.com/a/1jLDLWK0QboOu

 

 

***

 

 

Paper: Refined cyclic R-curve determination through residual crack tip stress reduction by annealing

 

Das Ausbreitungsverhalten von kleinen Ermüdungsrissen in hochfesten Werkstoffen, wie zum Beispiel Schnellarbeitsstählen für die Metallverarbeitung, ist noch nicht ausreichend erforscht, um deren Ermüdungseigenschaften durch wissensbasiertes Design zu optimieren. Deshalb haben Lukas Walch, Thomas Klünsner, Gerald Ressel und Stefan Marsoner am Materials Center Leoben sowie weitere Forscher am Erich Schmid Institut und bei voestalpine Böhler Edelstahl ein Verfahren entwickelt, das eine wesentlich genauere Bestimmung des Widerstandes gegen Ermüdungsrissausbreitung ermöglicht. Das ermöglicht die Entwicklung neuer, schadensresistenterer Schnellarbeitsstähle für eine ressourceneffizientere Herstellung unserer Alltagsgüter.

Nähere Informationen: https://authors.elsevier.com/a/1jLDLWK0QboOu